Heat Resistant Conveyor Belt for Rubber Industrial Conveyor Belt

• Type: Every
• Material: Rubber
• Inside Material: Fabric
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: RPR010
• Feature: Oil-Resistant, Acid And Alkali Resistant, Tear-Resistant, Heat-Resistant, Cold-Resistant, Wear-Resistant
• Tensile Strength: Strong
• Transport Package: General
• Specification: 1000*1500
• Trademark: Respower
• Origin: China
• HS Code: 40101200
• Package Size: 1000.00cm * 1000.00cm * 180.00cm
• Package Gross Weight: 10.000kg
• Lead Time: 7 days (1 - 1000 Meters) ; To be negotiated ( > 1000 Meters)

Product Description

The belt carcass of this product is EP fabric of high modulus,low shrink,and high breaking tensile strength.Cover rubber of this product uses EPDM rubber or Chloro-butyl rubber that has very good high temperature resistance.the belt is made with extra care after mixing rubber with high temperature resistant materials,assembling and vulcanizing.

The carcass of this product has very high adhesion after the special treatment of coating and shaping.Under normal working temperature of below 180ºC,the belt is low in elongation,excellent in anti-abrasion,and can bear 250ºChigh temperature for a short time.The belt is suitable for use in cement,metallurgical and steel industry.
Physical property indexes
 

Product features

 

• • Suitable for conveying hot material like powder or clump materials at high temperature.
  • Ideal for conveying sintered ores, cokes, soda ash, chemical fertilizer, slag and foundry.
  • It can resist high temperature.
  • The rubber compound used in the cover have been designed to avoid premature aging due to contact with any source of heat.
  • he belt carcass of this product is EP fabric of high modulus, low shrink, and high breaking tensile strength.
  • Cover rubber of this product uses EPDM rubber or chlorobutadiene rubber that has very good high temperature resistance.
  • The belt is made with extra care after mixing rubber with high temperature resistant materials, assembling and vulcanizing.
  • The belt can bear 250°C even 500°C high temperature for a short time.

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply N/mm	Cover to Ply N/mm	Ply to Ply
DIN 22102	Mpa	%	mm3	(≤1.5mm)	(>1.5mm)	N/mm
DIN 22102-Z	15	350	250	3.5	4.5	5
DIN 22102-W	18	400	90	3.5	4.5	5
DIN 22102-Y	20	400	150	3.5	4.5	5
DIN 22102-X	25	450	120	3.5	4.5	5

 

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply N/mm	Cover to Ply N/mm	Ply to Ply
AS 1332	Mpa	%	mm3	(≤1.9mm)	(>1.9mm)	N/mm
AS 1332-N	17	400	200	4	4.8	6
AS 1332-M	24	450	125	4	4.8	6
AS 1332-E	14	300	250	4	4.8	6
AS 1332-A	17	400	70	4	4.8	6

 

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply N/mm	Cover to Ply N/mm	Ply to Ply
SANS 1173	Mpa	%	mm3	N/mm		N/mm
A	18	400	70	5		7
C	20	400	150	5		7
M	25	450	120	5		7
N	17	400	150	5		7

 

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply N/mm	Cover to Ply N/mm	Ply to Ply
RMA	Mpa	%	mm3	(≤1.6mm)	(>1.6mm)	N/mm
RMA-I	17	400		3	4.4	4
RMA-II	14	400		3	4.4	4