Fabric 200-500 Sw Belt DIN-Z. X. W Straight Warp Cfw Conveyor Belt

• Type: Cfw
• Material: Rubber
• Inside Material: Every
• Shipping Cost: Estimated freight per unit.: about shipping cost and estimated delivery time.
• Currency: US$
• Return&refunds: You can apply for a refund up to 30 days after receipt of the products.
• Model NO.: RPR015
• Feature: Oil-Resistant, Acid And Alkali Resistant, Tear-Resistant, Heat-Resistant, Cold-Resistant, Wear-Resistant
• Tensile Strength: Strong
• Transport Package: General
• Specification: 1000*1500
• Trademark: Respower
• Origin: China
• HS Code: 40101200
• Production Capacity: 5000000 Meters/Year
• Package Size: 1000.00cm * 1000.00cm * 180.00cm
• Package Gross Weight: 10.000kg
• Lead Time: 7 days (1 - 1000 Meters) ; To be negotiated ( > 1000 Meters)

Product Description

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply N/mm	Cover to Ply N/mm	Ply to Ply
DIN 22102	Mpa	%	mm3	(≤1.5mm)	(>1.5mm)	N/mm
DIN 22102-Z	15	350	250	3.5	4.5	5
DIN 22102-W	18	400	90	3.5	4.5	5
DIN 22102-Y	20	400	150	3.5	4.5	5
DIN 22102-X	25	450	120	3.5	4.5	5

 

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply N/mm	Cover to Ply N/mm	Ply to Ply
AS 1332	Mpa	%	mm3	(≤1.9mm)	(>1.9mm)	N/mm
AS 1332-N	17	400	200	4	4.8	6
AS 1332-M	24	450	125	4	4.8	6
AS 1332-E	14	300	250	4	4.8	6
AS 1332-A	17	400	70	4	4.8	6

 

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply N/mm	Cover to Ply N/mm	Ply to Ply
SANS 1173	Mpa	%	mm3	N/mm		N/mm
A	18	400	70	5		7
C	20	400	150	5		7
M	25	450	120	5		7
N	17	400	150	5		7

 

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply N/mm	Cover to Ply N/mm	Ply to Ply
RMA	Mpa	%	mm3	(≤1.6mm)	(>1.6mm)	N/mm
RMA-I	17	400		3	4.4	4
RMA-II	14	400		3	4.4	4

Features
low elongation, excellent impact resistance, excellent anti-tearing performance, low rolling resistance, high adhesive strength.
 

CFW Fabric Technical data

Fabric Type		Breaking strength	Elongation at break	weight	thickness	width	Peel strength
		N/mm	%	g/m2	mm	mm	N/mm
CFW200	warp	>240	>15	650	0.85	800~1600	≥8
	weft	>80	≤45
CFW250	warp	>330	>15	810	1.1		≥8
	weft	>90	≤45
CFW300	warp	>350	>15	890	1.25		≥8
	weft	>100	≤45
CFW350	warp	>400	>15	1050	1.3		≥8
	weft	>105	≤45
CFW400	warp	>460	>15	1080	1.4		≥8
	weft	>110	≤45
CFW500	warp	>570	>15	1350	1.55		≥8
	weft	>120	≤45