Industrial Chemical Resistant Conveyor Belt for Conveyor

• Customization: Available
• Material: Rubber
• Feature: Oil-Resistant, Acid And Alkali Resistant, Tear-Resistant, Heat-Resistant, Cold-Resistant, Wear-Resistant
• Model NO.: RPR026
• Tensile Strength: Strong
• Transport Package: General
• Specification: 1000*1500
• Trademark: general
• Origin: China
• HS Code: 40101200
• Production Capacity: 5000000 Meters/Year
• Package Size: 1000.00cm * 1000.00cm * 180.00cm
• Package Gross Weight: 10.000kg
• Lead Time: 7 days (1 - 1000 Meters) ; To be negotiated ( > 1000 Meters)

Product Description

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply N/mm	Cover to Ply N/mm	Ply to Ply
DIN 22102	Mpa	%	mm3	(≤1.5mm)	(>1.5mm)	N/mm
DIN 22102-Z	15	350	250	3.5	4.5	5
DIN 22102-W	18	400	90	3.5	4.5	5
DIN 22102-Y	20	400	150	3.5	4.5	5
DIN 22102-X	25	450	120	3.5	4.5	5

 

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply N/mm	Cover to Ply N/mm	Ply to Ply
AS 1332	Mpa	%	mm3	(≤1.9mm)	(>1.9mm)	N/mm
AS 1332-N	17	400	200	4	4.8	6
AS 1332-M	24	450	125	4	4.8	6
AS 1332-E	14	300	250	4	4.8	6
AS 1332-A	17	400	70	4	4.8	6

 

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply N/mm	Cover to Ply N/mm	Ply to Ply
SANS 1173	Mpa	%	mm3	N/mm		N/mm
A	18	400	70	5		7
C	20	400	150	5		7
M	25	450	120	5		7
N	17	400	150	5		7

 

Standards	Cover Rubber			Adhesion
	Tensile Strength	Elongation at break	Abrasion	Cover to Ply N/mm	Cover to Ply N/mm	Ply to Ply
RMA	Mpa	%	mm3	(≤1.6mm)	(>1.6mm)	N/mm
RMA-I	17	400		3	4.4	4
RMA-II	14	400		3	4.4	4

Characteristics
The rubber cover, which is made from chemical resistant materials, has fine anti-chemical corrosiveness and good physical property.
It is specially made for those materials which would dissolve expand or corrode the belt.
It is suitable for conveying material with chemical corrosiveness in chemical factory, chemical fertilizer factory, paper mill, mining industry etc.
 

Technical indexes

 

Item			Tensile Strength /Mpa ≥	Elongation at break /% ≥	Abrasion /mm3 ≤	Hardness /(°) 10 -5	Ozone deterioration
COVER	Physical property	Before aging	14	400	250	60	no cracks
		After aging	12	340	-	65	-
	Acid and alkali resistance	Class	Soak liquid	Density	Soak conditions	Change rate before and after soak
					°C x h	Swelling rate	Change rate of tensile strength
		A1	HCL	18%	50°C x 96h	≤+10%	≤-10%
		A2	H2SO4	50%	50°C x 96h	≤+10%	≤-10%
		A3	NaOH	48%	50°C x 96h	≤+10%	≤-10%

Features: Excellent chemical resistance performance
Applicable environment: Chemical plant, chemical fertilizer plant, paper-making factory

Technical data:

Physical property of cover rubber under hot air accelerated aging test (test condition: 70ºC*96h)
 

ITEM	Breaking strength,MPa	Elongation at break,%	abrasion,mm3	hardness
				(°)
Performance before aging	≥14.0	≥400	≤250	60±5
Performance after aging	≥12.0	≥340	---	65±10
Note: When the thickness of the cover rubber is 0.8mm-1.6m, the sample thickness can be the maximum cut length, the tensile strength and the elongation at break are allowed to be 15% lower than those in the table.